Superconductive photoconductive-substance of the Y-Ba-Cu-O system and a method for producing the same

ABSTRACT

The disclosed substance has a general chemical formula of Y 3-x  -Ba x  -Cu y  -O z , x being 0 to 2, y being 3 to 6, and z being 6 to 12 (but excluding compositions with x=2, y=3 and z=6.75-6.97). At a temperature below 90-95 K, the disclosed substance shows superconductive photoconductivity or even both superconductivity, either real or potential, and photoconductivity in response to incident exciting light in a wavelength range of 420 to 640 nm. The substance is produced by heating a mixture of starting material therefor at 750°-1,050° C. for 1-10 hours so as to cause solid phase reaction, cooling gradually, shaping under pressure, sintering at 670°-1,050° C., and cooling either quickly at a rate of 2,000°-900° C./sec or slowly at a rate of 150°-200° C./hour.

This is a continuation of application Ser. No. 07/244,240, filed Sep. 14, 1988 abandoned.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to superconductive photoconductive-substance of the Y-Ba-Cu-O system defined to be photoconductive substance correlative with superconductivity whose composition is outside but includes even areas continuously close to that of regular oxide superconductors. Experiments on the optical properties, especially on the photoconduction in response to high-speed pulses, e.g. a pulsed light out of a dye laser, of substance with a chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z) revealed an unexpected correlation between the superconductivity and the photoconductivity of the substance.

The invention also relates to a method for producing substance with a chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), in which method either x and y of the chemical formula are controlled for instance by varying x from 0 to 2 while keeping y=3, or z of the chemical formula is controlled by quick cooling or slow cooling while keeping x and y constant such as x=2 and y=3. When the substance has a low value of x near x=0 or is cooled quickly, the substance becomes a photoconductive insulator or semiconductor. On the other hand, when the substance has a value of x near x=1 and is cooled slowly, the substance becomes a photoconductive superconductor.

The substance in the invention is expected to be useful in developing new industrial field of "Superconductive Opto-Electronics".

2. Related Art Statement

There has been no publications on such a system of substance which has superconductive photoconductivity or both superconductivity and inherent photoconductivity.

Conventional superconductors are metals or alloys in the main. Recently, much attention has been paid to high-temperature oxide superconductors, such as superconductors of the Y-Ba-Cu-O group, and considerable amounts of additives such as barium (Ba) and strontium (Sr) are used to raise the superconductive critical temperature (T_(c)). Studies and measurements on the optical properties of the superconductors at and in the proximity of visible wavelengths have been limited to the study of reflection and scattering of light therefrom due to a part of the metallic properties of such substance.

It has been believed that light is simply reflected from or scattered by the surface of a superconductor and is not allowed to enter therein. Study of optical properties, except the phenomena of reflection and scattering, has been treated as a completely different field from that of superconductivity in academic institutions, domestic and abroad, and in international conferences.

On the other hand, if any substance having superconductive photoconductive capability or even both superconductive capability and photoconductive capability at the boundary compositions is produced, a number of new electronic and optoelectronic devices may be developed; for instance, a superconductive phototransistor, a "superconductive optical computer" with a combined characteristics of the "superconductive computer" based on the currently studied Josephson devices and the "optical computer" proposed in optoelectronics, "superconductive optical fiber", and the like.

SUMMARY OF THE INVENTION

Therefore, an object of the present invention is to provide superconductive photoconductive-substance which reveals superconductive photoconductivity or both superconductivity and photoconductivity at a temperature below its critical temperature for superconductivity.

The superconductive photoconductive-substance according to the invention has a general chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), x being 0 to 2, y being 3 to 6, and z being 6 to 12 (but excluding compositions with x=2, y=3 and z=6.75-6.97). The substance of the invention shows superconductive photoconductivity or even both superconductivity and photoconductivity at a temperature below 90-95K, the photoconductivity being valid in a wavelength range of 420 to 640 nm. The superconductivity of the substance of the invention may be either potential or real.

Another object of the present invention is to provide a method for producing the above-mentioned superconductive photoconductive-substance which reveals superconductive photoconductivity or even both superconductivity and photoconductivity at a temperature below its critical temperature for superconductivity.

With a method according to the invention for producing the superconductive photoconductive-substance with a general chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), x being 0 to 2, y being 3 to 6, and z being 6 to 12 (but excluding compositions with x=2, y=3 and z=6.75-6.97) a mixture of starting materials for a composition of the above-mentioned chemical formula is heated at 750°-1,050° C. for 1-10 hours so as to cause solid phase reaction in the mixture. The heated mixture is cooled gradually after that the cooled mixture is shaped under pressure. The shaped mixture is sintered at 670°-1,050° C., and then cooled either quickly at a rate of 2,000°-900° C./sec or slowly at a rate of 150°-200° C./hour. The substance thus produced reveals superconductive photoconductivity or both superconductivity and photoconductivity.

The reason for limiting the composition of the substance of the invention to the above-mentioned general chemical formula is in that the substance of such composition reveals superconductive photoconductivity or even both superconductivity and photoconductivity provided that it is treated by the method of the invention; namely, the method comprising steps of heating at 750°-1,050° C. for 1-10 hours so as to cause solid phase reaction in a starting material mixture, cooling gradually the heated mixture, shaping the cooled mixture under pressure, sintering the shaped mixture at 670°-1,050° C., and cooling the sintered substance either quickly at a rate of 2,000°-900° C./sec or slowly at a rate of 150°-200° C./hour.

The inventors have found that, in the substance with a general chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), if x is zero (x=0) or close to zero, the substance becomes insulating and shows semiconductive properties as well as photoconductive properties for certain wavelengths of light. On the other hand, if x departs from 0 and increases toward 2, the superconductive properties of the substance becomes more apparent while the photoconductive properties of the substance is maintained. It is noted that when the composition of a substance is such that x=2, y=3 and z is 6.75 to 6.97 in the chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), the substance with such composition shows only superconductive properties, so that such composition is excluded from the scope of the composition of the invention.

Of the substance according to the invention, substance of insulating type has for instance x=0, y=3-6 and z of 7.5 to 12 in the above chemical formula, while substance of superconductive type has for instance x=2, y=3 and z of 6.5 to 6.97 in the above chemical formula. It is an important finding of the inventor that even the above substance of insulating type has such photoconductivity which depends both on temperature and wavelength of exciting light, and the manner of its dependence on temperature and wavelength suggests a potential correlation with superconductivity in the insulating type substance. The present invention is based on such finding.

BRIEF DESCRIPTION OF THE DRAWINGS

For a better understanding of the invention, reference is made to the accompanying drawings, in which:

FIG. 1A is a simplified block diagram showing principles of a photoconductivity [(a) dotted arrows] and the Hall effect [(b) solid arrows] measuring circuit which uses blocking electrodes and light pulses;

FIG. 1B illustrates a time sequence charts showing waveforms of signals in the circuit of FIG. 1A;

FIG. 2A shows sectional views of an essential part of a static susceptibility measuring device using a microwave SQUID (Superconducting Quantum Interference Device);

FIG. 2B is a block diagram of the measuring system with the device of FIG. 2A;

FIG. 2C is a block diagram of the feedback system with the device of FIG. 2A;

FIG. 3A is a graph showing the wavelength-dependence of photoconductive response Q (λ, T) of the superconductive photoconductive-substance with Y_(3-x) -Ba_(x) -Cu_(y) -O_(z) for the case of x=0, y=6 and z≃10.5;

FIG. 3B is a similar graph of FIG. 3A except for the case of x=0, y=3 and z≃7.5;

FIG. 3C is a similar graph as FIG. 3A except for the case of x=1, y=3 and z≃6.6;

FIG. 4 shows waveforms of signals induced and transferred by a signal detecting coil to the microwave SQUID for different specimens of the substance Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), which waveforms represent the positive or negative sign and magnitude of magnetization in the specimens;

FIG. 5A is a graph showing the temperature-dependence of photoconductive response Q (λ, T) of the superconductive photoconductive-substance Y_(3-x) -Ba_(x) -Cu_(y) -O_(z) for the case of x=0, y=3 and z≃7.5;

FIG. 5B is a similar graph as FIG. 5A except for the case of x=1, y=3 and z≃6.6; and

FIG. 5C is a graph showing the temperature-dependence of dark resistance R (T) of the superconducting photoconductive-substance and superconducting substance Y_(3-x) -Ba_(x) -Cu_(y) -O_(z) for both the case of x=1, y=3 and z≃6.6, and the case of x=2, y=3 and z=6.9, respectively.

DESCRIPTION OF THE PREFERRED EMBODIMENT

Most of conventional oxide compounds such as Y₃ -Cu₆ -O_(z) (z being 6 to 12) and Y_(3-x) -Ba_(x) -Cu₃ -O_(z-y) are normally semiconductors at the ground state, e.g., at low temperatures and in the dark. An elementary excitation can be created by giving the many-body ground state an appreciable amount of energy with relevant magnitude of momentum. Usually, for superconductors, these excitations beyond the energy gap destroy the superconductive ground state in the BCS theory. There is a possibility, however, to create a coherent state of elementary excitations above the ground state of insulating semiconductors such as bipolarons and excitons even in a thermally non equilibrium state. We have found a new substance as an outcome of studies in fundamental physics and applied physics from the standpoint of the elementary excitation concept, in a sense parallel to, but rather orthogonal to the trend of studies of high-T_(c) (critical temperature) superconductors. Namely, our finding relates to substance whose composition does not result in perfect superconductor, but the substance has a composition close to that of superconductor and reveals superconductive photoconductivity or even both superconductivity and photoconductivity. The present invention has been completed based on that finding.

The invention will be described in further detail by referring to embodiments.

EMBODIMENTS

The composition of the substance found by the inventors can be expressed by a chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z). The inventor has tried to seek into details of the complete scheme of a phase diagram of Y_(3-x) -Ba_(x) -Cu_(y) O_(z).

A large number of specimens of Y-Cu-O and Y-Ba-Cu-O systems were made from the powders of Y₂ O₃, BaCO₃ and CuO by using the method already described in numerous references. For instance, primary sintering of a mixture of starting materials for a composition of said chemical formula was effected at 750°-1,050° C. for 1-10 hours so as to cause solid phase reaction in the mixture. After being cooled gradually, the sintered mixture was shaped under pressure, and secondary sintering was effected at 670°-1,050° C. The specimens were then annealed at 600°-700° C. and cooled slowly. The composition of the starting material was studied in detail, and the composition of the specimen was selected to be close to regular superconductors in such a manner that it became more or less controllable in a range outside that of the latter. Besides, the value of z in the above chemical formula was controlled by carefully regulating the method and speed of cooling.

Specimens No. S20, No. S21 and No. S22 were prepared in the above-mentioned manner.

Specimen No. S61 with a composition of Y₃ -Cu₃ -O₇.5 was prepared by primary sintering of a starting mixture of the above composition at 1,000°-1,050° C. for 2 hours, slow cooling, shaping under pressure, secondary sintering at 1,000°-1,050° C. for 2 hours, cooling, annealing at 700° C. for 2 hours, and slow cooling.

Since specimens of the Y₃ -Cu₃ -O_(z), Y₃ -Cu₆ -O_(z) and Y_(3-x) -Ba_(x) -Cu_(y) -O_(z) systems within a certain part of the values of x, y and z became highly insulating or at least semiconducting at low temperatures, the conventional techniques for resistivity measurements encountered several serious difficulties, especially such as those associated with the non-ohmic contact electrodes, the build-up of space charge and with the low signal-to-noise ratio due to low carrier density in high-impedance materials.

In the experiments of the inventors, two types of techniques were adopted for resistivity or/and conductivity measurements. First, for insulating specimens (ρ≧10⁸ Ω·cm) such as No. S22, a fast pulse technique with blocking electrodes as shown in FIG. 1A was adopted. Referring to FIG. 1B, the difficulties noted above were overcome by using a pulsed dye laser of 3 ns width at a repetition rate of 13 Hz in the dark synchronized with pulse electric fields up to E≃5 kV/cm of 10 ms duration for measuring photoresponse, as shown in FIG. 1B. Second, for moderately conducting specimens (ρ≧(10⁻² -10⁻¹) Ω·cm) at 300K such as SpeCimens No. S20 and No. S21, resistivity measurements were performed by adopting the usual four-probe method in the dark without using any light.

The specimen No. S20 was made by mixing 0.40 g of Y₂ O₃, 1.40 g of BaCO₃ and 0.85 g of CuO, and sintering the mixture. The specimen No. S61 was made by mixing 2.26 g of Y₂ O₃ and 1.59 g of CuO, and sintering the mixture so as to produce Y₃ -Cu₃ -O_(z). The specimen No. S21 was made by mixing 0.40 g of Y₂ O₃, 0.35 g of BaCO₃ and 0.425 g of CuO, and sintering the mixture so as to produce Y₂ -Ba₁ -Cu₃ O_(z). The specimen No. S22 was made by mixing 0.72 g of Y₂ O₃ and 1.00 g of CuO, and sintering the mixture so as to produce Y₃ -Cu₆ -O_(z). Here, z represents the amount of oxygen in the substance, and it varies depending on the sintering conditions so as to produce a variety of final products.

Static magnetic susceptibility or magnetization itself was measured in weak fields up to H≃50 Oe by using a microwave SQUID (Superconducting Quantum Interference Device) at 9 GHz as shown in FIG. 2A and FIG. 2B. The system was normally operated in the mode locked to the Q-pattern as shown in FIG. 2C. The bandwidth of the system covered from d.c. to 200 kHz, and the slew rate was set at about 10⁴ φ₀ /sec.

Spectral responses were studied by selecting the wavelength λ from a dye laser with a resolution Δλ-1 nm while using an appropriate normalization procedure for incident power from the laser and spectral sensitivity of the pyroelectric detector. A possibility of heating of the specimens by light excitation was minimized and estimated to be negligible. Photocarrier density was of the order of (10⁶ to 10⁸)/cm³ averaged over a specimen. All photosignals were normally detected in the synchronized mode by using the Boxcar integrator.

EXPERIMENTAL RESULTS

The inventors observed definite signals of photoconductivity of specimen No. S22 Y₃ -Cu₆ -O_(z) and all specimens Y_(3-x) -Ba_(x) -Cu₃ -O_(z) except No. S20 (with x=2) by using the transient pulse technique described above.

Firstly, the dependence of photoconductivity Q(λ,T,E,H) on E was found to be almost linear up to E≃5 kV/cm at 77K. No appreciable magnitude of the transverse and longitudinal magneto-resistance in Q(λ,T,E,H) has been observed up to H≃15 kOe at 77K. FIG. 3A illustrates a typical spectrum of pulse-excited transient photoresponse Q(λ,T) of specimen No. S22 Y₃ -Cu₆ -O_(z) (z being about 10.5) over wavelengths 460 to 640 nm, FIG. 3B illustrates a similar spectrum of specimen No. S61 Y₃ -Cu₃ -O_(z) (z being about 7.5), and FIG. 3C illustrates a similar spectrum of specimen No. S21 Y₂ -Ba₁ -Cu₃ -O_(z) (z being about 6.6). The inset of FIG. 3A illustrates well established reference data of photocurrent in Cu₂ O reported by Gross.

Secondly, it was confirmed that the magnetizations M(T,H) of specimen No. S22 Y₃ -Cu₆ -O_(z) (z being about 10.5) and specimen No. S61 Y₃ -Cu₃ -O_(z) (z being about 7.5) were clearly paramagnetic or at least positive at 4.2K and H=48 Oe, as shown in FIG. 4. Most remarkably, the values of magnetizations M(T,H) of specimen No. S20 Y₁ -Ba₂ -Cu₃ -O_(z) and particularly even specimen No. S21 Y₂ -Ba₁ -Cu₃ -O_(z) (z being about 6.6) at 4.2K definitely indicated negative diamagnetic signals which were characteristic to superconducting specimens. The magnitude of magnetization of specimen No. S21 was about one thirtieth (1/30) of that of specimen No. S20.

Thirdly, temperature dependence of the pulse-excited transient photoresponse Q(λ,T) in the region between λ≃420-640 nm, i.e., the visible wavelength region, were studied both for an insulating specimen No. S61 and for a superconducting specimen No. S21 as illustrated in FIG. 5A and FIG. 5B, respectively. Surprisingly, there definitely exists a remarkable similarity between general features of the transient photoresponse Q(λ,T) for No. S61 and No. S21, regardless of the huge difference in dark resistivity P(T) as illustrated only for No. S21 in FIG. 5C. Dark resistivity ρ(T) of No. S61 is too large to be shown. As the temperature decreases, it is clearly recognized that "photoconductivity" starts to reveal in the proximity of 100K, assumes maximum value at 70-80K and maintains a comparatively flat level until about 10K, and then the transient photoresponse Q(λ,T) rapidly decreases for superconducting specimen No. 21, whereas it still increases for insulating specimen No. 61.

Finally, the resistivity ρ(T) in the dark of the Superconducting specimen No. S21 Y₂ -Ba₁ -Cu₃ -O_(z) and that of specimen No. S20 Y₁ -Ba₂ -Cu₃ -O_(z) are displayed in FIG. 5C as functions of temperature T(K). One immediately notices that both of those specimens become superconductive below T_(c) =50-90K. No photoconductive signals of photoresponse Q(λ,T) have been observed for the specimen No. S20.

It is by no means easy to interpret these facts. At 300K, the specimen No. S22 Y₃ -Cu₆ -O_(z) is clearly an insulator and the specimen No. S21 Y₂ -Ba₁ -Cu₃ -O_(z) is semiconductive. In the specimen No. S21, the photoconductivity observed with the blocking electrodes is compatible with superconductivity as illustrated in FIG. 5B probably due to the insulating part of specimen No. S21 as also noted via the value of magnetization. Surprisingly, there exists an occurrence of photoconductivity potentially correlative with superconductivity underlying even in insulating specimen No. S61 as displayed in FIG. 5A.

DISCUSSION

It is a widely recognized fact that the specimens Y_(3-x) -Ba_(x) -Cu₃ -O_(z) such as No. S21 usually have dark green colors. A specimen of Y₃ -Cu₆ -O_(z) such as No. S22 looks blue green. The spectral response of photoconductivity Q(λ,T) in FIGS. 3A, 3B and 3C strongly suggests that there exists a region of the Cu₂ O-like state at least in the specimen of Y₃ -Cu₆ -O_(z) and possibly even in those of Y_(3-x) -Ba_(x) -Cu₃ -O_(z), if not atomic layers. As the signals Q(λ,T) are clearly observed, one has to recognize that either conduction electrons or positive holes or even both are mobile in insulating Y-Cu-O and Y-Ba Cu-O specimens. The sign of the photoresponse in the Dember effect indicates that the dominant photocarriers are positive holes.

Optical absorption and photoconductivity of Cu₂ O have been thoroughly analyzed in terms of the exciton theory. We can recognize a few fine structures due to the excitons in the spectra of Q(λ) both of Y₃ -Cu₆ -O_(z) and of Y_(3-x) -Ba_(x) -Cu₃ -O_(z) similar to those of Cu₂ O. Thus, we can reasonably conceive that there exists at least a finite fraction of the Cu₂ O-like phase which cannot be ignored in the Y Cu-O and Y-Ba-Cu-O systems where the photoexcited electrons and holes are definitely mobile, irrespective of a certain difference of the crystal structures. Data obtained by experiments of XPS (X-ray Photoelectronic Spectrography), EXAFS (Extended X-ray Absorption Fine Structures) and XANES (X-ray Absorption Near Edge Structures) revealed the existence of monovalent Cu¹⁺ ions besides divalent Cu²⁺ ions, and trivalent Cu³⁺ ions. Results of the energy band calculation and an evaluation of the density of states (DOS) also indicate similar tendencies.

A conduction electron or a positive hole in standard types of Cu₂ O crystals has been reported to have a rather weak coupling constant α with the LO-phonons (α=0.14-0.18, being rather large as compared with that of regular III, IV group semiconductors) in the polaron formation, which results in a "large polaron". Actually, the cyclotron resonances of conduction electrons and positive holes have been observed at 1.2-20K. On the other hand, however, it must have a much larger effective dielectric constant κ and a coupling constant α in the Cu₂ O-like part, possibly enhanced due to an order of oxygen vacancy in the Y₃ -Cu₆ -O_(z) and Y_(3-x) -Ba_(x) -Cu₃ -O_(z) specimens as a series of ferroelectric materials with a large static dielectric constant. Originally, Muller with Bednorz started to study oxides which are likely to have strong electron-phonon interaction and are good candidates for polaron formation due to lattice deformation caused by the Jahn-Teller effect. The dynamical effects of the polaron, whether it is a "large polaron" with the LO-phonons, a "small polaron" due to the Jahn-Teller effect or possibly an intermediate one due to both effects, they must be substantial as well as the "electronic polaron effect". They, i.e., those polarons due to phonons and due to electrons, are probably effective in a coherently hybridized form of these elementary excitations.

Therefore, we may reasonably conceive of potential roles of an ensemble of polarons, whether large or small, and excitons in the phenomena of superconductivity here. The ensemble of united polarons and excitons are probably a set of bipolarons, polaronic excitons and/or excitonic polarons due to the dynamical electron-phonon and electron correlation effects. These polarons and excitons had yielded out of the optical transition from the hybridized 2p-Oxygen and 3d-Cu valence bands leaving (3d)⁹ positive holes to the 4s-Cu conduction band creating a (4s)¹ conduction electron together with the LO-phonon interaction. A polaron can be created either by the optical excitation here or substitution of Y by Ba especially in the Y-Cu-O system. As indicated in FIG. 5A, photosignals or photoresponse Q(λ,T) in the Y-Cu-O system reflect the occurrence of superconductivity in the Y-Ba-Cu-O system. Similar phenomena have been observed also in the La-Cu-O systems. Consequently, the inventors believe that these studies of elementary excitations here must reveal the nature of the superconducting ground state. To the best knowledge of the inventors, this is the first clear experimental indications of the polaron and exciton mechanism, i.e., "the exiton mediated bipolaron mechanism", displayed in the high-T_(c) superconductivity and the perfect diamagnetism.

EFFECT OF THE INVENTION

As described in detail in the foregoing, the inventors have observed, for the first time, an unexpected accordance of the onsets of profound significance, i.e., "correlation of photoconductivity with superconductivity and perfect diamagnetism", at least in substance with a chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), x being 0 to 2, y being 3 to 6, and z being 6 to 12 (but excluding superconductive compositions with x=2, y=3 and z=6.75-6.97). A method for producing the above substance has been also developed.

It should be noted that the invention is an outcome of theoretical and experimental studies on the "dynamical mechanism of polarons and excitons" for "high-temperature superconductivity" as proposed by the inventors. The proposed substance of the invention will open a new scientific and industrial field, to be named as "Superconductive Opto-Electronics", wherein superconductivity is directly controlled by light.

Although the invention has been described with a certain degree of particularity, it must be understood that the present disclosure has been made only by way of example and that further numerous changes in details may be resorted to without departing from the scope of the invention as hereinafter claimed. 

What is claimed is:
 1. A method for varying the electric conductivity of a photoconductive substance of the Y-Ba-Cu-O system having a general chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), x being 0 to 1, y being 3 to 6, and z being 6 to 12, comprising the step of exposing the substance to incident light of wavelength 420 to 640 nm at a temperature below 90-95K.
 2. A method as in claim 1, wherein the temperature at which the photoconductivity of the photoconductive substance emerges and increases corresponds to the onset temperature of superconductivity in a superconductive substance of the Y-Ba-Cu-O system.
 3. A method as in claim 1, wherein the electric conductivity of the photoconductive substance is increased upon exposing the photoconductive substance to incident light of wavelength 420 to 640 nm at a temperature below 90-95K.
 4. A method as in claim 1, wherein said exposing step is carried out by exposing the photoconductive substance to light from a dye laser.
 5. A method as in claim 4, wherein said light from a dye laser is pulsed light.
 6. A method as in claim 5, wherein said pulsed light is of 3 ns width and has a pulse rate of 13 Hz.
 7. A method as in claim 1, wherein said exposing step generates a photocarrier density in the photoconductive substance of from (10⁶ to 10⁸)/cm³ averaged over the substance.
 8. A method as in claim 1, wherein said photoconductive substance is exposed to light having an intensity of at least 2×10³ W/cm³ ·nm.
 9. A method as in claim 1, wherein said photoconductive substance is shielded from light other than that of the exposing means.
 10. A method for eliciting the photoconductivity Q(λ,T) of a photoconductive substance of the Y-Ba-Cu-O system having a general chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), x being 0 to 1, y being 3 to 6, and z being 6 to 12, comprising the steps of exposing the substance to incident light of wavelength (λ) in the range of 420 to 640 nm at a temperature (T) below 90-95K, wherein said substance is an insulator or a semiconductor in the dark.
 11. A method as in claim 10, wherein the temperature at which the photoconductivity Q(λ,T) of the photoconductive substance emerges and increases corresponds to the onset temperature (T) of superconductivity in a superconductive substance of the Y-Ba-Cu-O system.
 12. A method as in claim 10, wherein the photoconductivity Q(λ,T) of the photoconductive substance is increased upon exposing the photoconductive substance to incident light of wavelength (λ) in the range of 420 to 640 nm at a temperature (T) below 90-95K.
 13. A method as in claim 10, wherein said exposing step is carried out by exposing the photoconductive substance to light from a dye laser.
 14. A method as in claim 12, wherein said light from a dye laser is pulsed light.
 15. A method as in claim 13, wherein said pulsed light is of 3 ns width and has a pulse rate of 13 Hz.
 16. A method as in claim 10, wherein said exposing step generates a photocarrier density in the photoconductive substance of from (10⁶ to 10⁸)/cm³ averaged over the substance.
 17. A method as in claim 9, wherein said photoconductive substance is exposed to light having an intensity of at least 2×10³ W/cm³ ·nm.
 18. A method as in claim 9, wherein said photoconductive substance is shielded from light other than that of the exposing means.
 19. A method for varying the flow of electric current in an electrical circuit comprising a photoconductive substance of the Y-Ba-Cu-O system in the conduction path thereof having a general chemical formula of Y_(3-x) -Ba_(x) -Cu_(y) -O_(z), x being 0 to 1, y being 3 to 6, and z being 6 to 12, comprising the step of exposing the substance to incident light of wavelength in the range of 420 to 640 nm at a temperature (T) below 90-95K. 